Resumen:
The purpose of this work is to determine the effect caused by the use of borax as a flux in the characteristics of lead and caustic sodium glasses according to the plate casting technique. For the following practical case, a literature review was carried out on the raw materials involved in the formulation of the glass, as well as knowing the energy problems that arise in the casting process if borax is not used to reduce the amount of useful energy for carry out this process. Types of glass such as lead and caustic sodium use pure reagents in their composition (close to 95%) and a different formulation because the application of each type is specific. For lead glass, lead oxide (PbO) is used, with Pb+2 providing stability to the glass, however, for caustic soda glass, it incorporates alumina, which offers greater resistance to the glass.
Descripción:
El propósito del presente trabajo es determinar el efecto que causa el uso de bórax como fundente en las características de vidrios de plomo y sódico cáustico según la técnica de colado en placas. Para el siguiente caso práctico se realizó una revisión bibliográfica sobre las materias primas que interviene en la formulación del vidrio, así también conocer la problemática energética que se presenta en el proceso de fundición si no se usa el bórax para disminuir la cantidad de energía útil para llevar a cabo dicho proceso. Los tipos de vidrios como el de plomo y sódico cáustico utilizan en su composición reactivos puros (cerca del 95%) y una formulación diferente debido a que la aplicación de cada tipo es específica. Para el vidrio de plomo se usa el óxido de plomo (PbO) siendo el Pb+2 quien brinda la estabilidad al vidrio, no obstante para el vidrio sódico cáustico incorpora alúmina que ofrece mayor resistencia al vidrio.
Excepto si se señala otra cosa, la licencia del ítem se describe como openAccess